High quality plastic mould steel plate Din 1.2311 tool steel

General Information:

Pre-hardened grade specially designed for the plastic mold industry deliver in hardened and tempered condition (300HB), subsequent heat treatment is not necessary. Specially employed for the plastic mold industry and adapted ford polishing and chemical etching (low sulphur content).

Comparable Standards:                                                                                                       

 Chemical Analysis (%):                                                                                                         

Heat treatment                                                                                                       

Annealing:

Heat to 720÷750°Cfor 2÷4 h furnace cool.

Stress relieving:

Up to 560÷600°C, hold for 2÷4h; furnace or still air cooling.

Hardening:

Preheating to 600÷650°C;

-   Heat to hardening temperature to 840÷870°C and hold at temperature.

-   Cooling in oil

Hardness after hardening: HRC 51

Tempering:

To be carried out after hardening in the range 580÷650°C for 25mm of thickness minimum 2h.

---------------------------------------------------------------------------------------------------------------------------------

Product and Service - category                                                                                                                

More photos from Neworigin special steel: 

Warehouse in Shenzhen:

Stockings and products:

Testing:

Test Equipments:

Sawing machine:  

Max sawing size: 800mm*6000mm

Office:

Factory:

Rolling:

Our own certifications: